Device for propagating light and method for fabricating a device

ABSTRACT

A device for propagating light is described, comprising: a substrate having a semiconductor material, an insulating layer, wherein the insulating layer is arranged on the substrate, a recess reaching through the insulating layer and into the substrate, wherein the recess is at least partially filled with a filler material, and a waveguide arranged in or on the filler material.

FIELD OF THE INVENTION

The invention relates to a device for propagating light and a method forfabricating a device for propagating light.

BACKGROUND

Photonic devices comprising a semiconductor are widely used in moderntelecommunication systems. Typically the light is transmitted in opticalfibers. Therefore, the light has to be coupled from a first photonicdevice into an optical fiber. After transmitting the light in theoptical fiber the light has to be coupled back to a second photonicdevice. Therefore, coupling light from and to an optical fiber is animportant aspect in the telecommunication field.

US 2013/0181233 A1 discloses a silicon photonics wafer that includes anactive silicon photonics layer, a thin buried oxide layer, and a siliconsubstrate is received. The thin buried oxide layer is located betweenthe active silicon photonics layer and the silicon substrate. Anelectrical CMOS wafer that includes an active electrical layer is alsoreceived. The active silicon photonics layer of the silicon photonicswafer is flip chip bonded to the active electrical layer of theelectrical CMOS wafer. The silicon substrate is removed exposing abackside surface of the thin buried oxide layer. A low-opticalrefractive index backing wafer is added to the exposed backside surfaceof the thin buried oxide layer. The low-optical refractive index backingwafer is a glass substrate or silicon substrate wafer. The siliconsubstrate wafer includes a thick oxide layer that is attached to thethin buried oxide layer.

BRIEF SUMMARY OF THE INVENTION

A device for propagating light comprises: a substrate having asemiconductor material, an insulating layer, wherein the insulatinglayer is arranged on the substrate, a recess reaching through theinsulating layer and into the substrate, wherein the recess is at leastpartially filled with a filler material, and a waveguide arranged in oron the filler material.

Further, a method for fabricating a device comprises: providing asubstrate having a semiconductor material, placing an insulating layeron the substrate, providing a recess reaching through the insulatinglayer and into the substrate, filling the recess at least partially witha filler material, and arranging a waveguide in or on the fillermaterial.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows a perspective view of a device for propagating light;

FIG. 2 shows a cross-sectional view of the device for propagating lightof FIG. 1;

FIG. 3 shows a cross-sectional view of a further device for propagatinglight;

FIG. 4 shows a cross-sectional view of a further device for propagatinglight;

FIG. 5 shows the device of FIG. 4 comprising a further waveguide;

FIG. 6 shows a top view of FIG. 5 with a tapered further waveguide;

FIG. 7 shows a cross-sectional view of a further device for propagatinglight;

FIG. 8 shows a cross-sectional view of a further device for propagatinglight coupled to a further waveguide; and

FIG. 9A to 9I show a method for fabricating a device for propagatinglight.

Similar or functionally similar elements in the figures have beenallocated the same reference signs if not otherwise indicated.

DETAILED DESCRIPTION OF THE EMBODIMENTS

FIG. 1 shows a perspective view of a device 1 for propagating light. Thedevice 1 comprises a substrate 2, an insulating layer 3, a recess 4 anda waveguide 5. The substrate 2 has a semiconductor material 16. Theinsulating layer 3 is arranged on the substrate 2. As can be seen inFIG. 1 the recess 4 reaches through the insulating layer 3 and into thesubstrate 2, wherein the recess 4 is filled with a filler material 6.The waveguide 5 is arranged on the filler material 6. For example, thesubstrate's semiconductor material 16 is oxidized such that the recess 4filled with the filler material 6, e.g. silicon dioxide, is obtained.The boundary of the recess 4 in the substrate 2 can be defined as theinterface 15 between the semiconductor material 16 and the fillermaterial 6.

Further, the recess 4 has a recess bottom 7. A distance 8 between thewaveguide 5 and the recess bottom 7 is larger than a thickness 9 of theinsulating layer 3. The waveguide 5 is used for propagating light alongthe waveguide 5.

FIG. 2 shows a cross-sectional view of the device 1 along line II-II ofFIG. 1. As can be seen the insulating layer 3 is arranged on thesubstrate 2. The recess 4 reaches through the insulating layer 3 andinto the substrate 2. The light travelling through the waveguide 5comprises a light mode 10. Part of the light intensity and light mode 10is within the waveguide 5. However, the light mode will also have acertain intensity outside the waveguide 5. Thereby, the intensitydecreases with increasing distance from the waveguide 5. The dotted lineillustrates that the light mode 10 has a certain intensity outside thewaveguide 5. However, there is no sharp limit or boundary where thelight mode 10 does not have any more any intensity. Nearly all intensityof the light mode 10 is within radius 11 of the light mode 10. Theradius 11 of the light mode 10 is less than half of the width 12 of therecess 4. Furthermore, the light mode 10 does not reach into thesubstrate 2.

As can be seen in FIG. 2 the radius 11 of the light mode 10 is largerthan the thickness of the insulation layer. If the waveguide 5 would bearranged on the insulation layer 3 in an area far away from the recess 4than the light mode 10 would reach into the substrate 2. However,because of the recess 4 the light mode 10 does not reach into thesubstrate 2. Therefore, an attenuation of the light travelling along thewaveguide 5 because of the substrate 2 can be avoided. The light mode 10does not feel the substrate 2 and the absorptive properties of thesubstrate 2.

The light mode 10 can be completely in the waveguide 5, the fillermaterial 6 and the area 13 above the waveguide 5 and the filler material6. Therefore, it is important that the filler material does not absorblight or at least does only absorb a very small amount of the light,most preferably the absorption is lower than the absorption of thesubstrate 2. Because of that the filler material is a non-absorbingmaterial, wherein non-absorbing has the meaning not light absorbing.

The filler material 6 can have a lower index of refraction than thesubstrate 2. Further, the index of refraction of the filler material 6can be lower than the index of refraction of the material of thewaveguide 5. This helps to confine more light of the light mode 10 inthe waveguide 5. As a result this means a lower loss of light due toabsorption of light outside the waveguide 5.

The recess 4 can be formed such that a distance 14 between the waveguide5 and an interface 15 between the semiconductor material 16 and thefiller material 6 is larger than a predetermined distance. Thepredetermined distance can be calculated, for example, when the device 1is designed. Further, the predetermined distance is the distance whichis needed to keep the light mode 10 within the area of the fillermaterial 6. Further, the predetermined distance can be larger than theradius 11 of the light mode 10.

As can be seen in FIG. 2 the recess 4 comprises a first side wall 17 anda second side wall 18. The waveguide 5 can be arranged such that adistance 19 between the waveguide 5 and the first side wall 17 equals adistance 20 between the waveguide 5 and the second side wall 18.

The insulating layer 3 can be a buried silicon dioxide layer. The fillermaterial 6 and the insulating layer 3 can comprise the same material.This material can be silicon dioxide or other materials having a lowerindex of refraction than the substrate 2. The substrate 2 can comprisesilicon. Using these materials allows fabricating the device 1 using thestandard complementary metal-oxide-semiconductor technology (CMOStechnology).

The waveguide 5 can comprise silicon, polysilicon or a polymer. In analternative, the waveguide can consist of one of the group of silicon,polysilicon or a polymer. Furthermore, the waveguide 5 can comprise acladding 52. The cladding 52 is optional and is therefore indicated witha dashed line in FIG. 2. As can be seen in FIG. 2 the cladding is on thetop surface 53 and on the side surfaces 54 of the waveguide 5. In analternative, the cladding 53 is only on the top surface 53 of thewaveguide 5. In a further alternative, the waveguide 5 is surrounded bya cladding 52.

The locally increased thickness enables a larger radius 11 of the lightmode 10. If the filler material 6 and the material of the insulatinglayer 3 are the same material than in principle the thickness of theburied oxide layer is locally increased.

FIG. 3 shows a cross-sectional view of a further device 1 forpropagating light. In contrast to the device 1 shown in FIG. 2 in thedevice 1 shown in FIG. 3 the waveguide 5 is arranged within the fillermaterial 6. The recess 4 is partly filled with the filler material 6.The recess 4 is formed such that a distance 14 between the waveguide 5and the interface 15 between the semiconductor material 16 and thefiller material 6 is larger than the predetermined distance. Thereby,the predetermined distance is the distance which is necessary to keepthe light mode 10 within the area of the filler material 6.

Preferably, the waveguide 5 is arranged such that the distance 19between the waveguide 5 and the first side wall 17 equals the distance20 between the waveguide 5 and the second side wall 18. However,arranging the waveguide 5 in the center between the first side wall 17and the second side wall 18 is not necessary.

FIG. 4 shows a cross-sectional view of a further device 1 forpropagating light. In contrast to the device 1 depicted in FIG. 3 thedevice 1 depicted in FIG. 4 shows a recess 4 which has a tapered form 21in the substrate 2 in a direction from the waveguide 5 towards thesubstrate 2.

The recess 4 has straight sidewalls 22 in the insulating layer 3.Further, in the substrate 2 the recess 4 has tapered sidewalls 23. Thefiller material 6 can be a fast grown oxide, which is thermally grown ina dry or wet atmosphere. Therefore, because of the way of depositing thefiller material 6, the filler material 6 can provide tapered sidewalls24 in the insulating layer 3. As can be seen in FIG. 4 the waveguide 5is arranged on the filler material 6. The remaining areas 25 betweenfiller material 6, insulating layer 3 and waveguide 5 can be filled withthe same material as is also used for the insulating layer 3. Asmentioned before also the filler material 6 and the material of theinsulating layer 3 can be the same.

The tapered form 21 in the substrate 2 is well suited to fit the shapeof the light mode 10. Since for the filler material 6, the material ofthe areas 25 and the material of the insulating layer 3 the samematerial can be used it is no problem if the light mode 10 reaches intothe insulating layer 3 or the areas 25.

FIG. 5 shows the device 1 of FIG. 4 comprising a further waveguide 26.The further waveguide 26 is arranged above the waveguide 5. When thewaveguide 5 and the further waveguide 26 are close to each otheradiabatic coupling of light from one waveguide 5, 26 to the otherwaveguide 26, 5 is possible. In an alternative, the waveguide 5 and thefurther waveguide 26 are in contact with each other. In a furtheralternative, there may also be a gap between the waveguide 26 (which cancomprise a polymer) and the waveguide 5 (which can comprise silicon).This gap is called “bondline”.

In an alternative, the further waveguide 26 can be arranged below thewaveguide 5. In this case the waveguide 5 is arranged as depicted inFIG. 2. Further, in this case the further waveguide 26 is then arrangedin the filler material 6.

FIG. 6 shows a top view of FIG. 5. However, in contrast to FIG. 5 thewaveguide 5 of FIG. 6 comprises a tapered section 27. Since thewaveguide 5 can not be seen from the top view because of the furtherwaveguide 26, the waveguide 5 is depicted with a dashed line. Thewaveguide 5 extends in a longitudinal direction 28. In the area wherethe light adiabatically couples from one waveguide 5, 26 to the otherwaveguide 26, 5 the waveguides 5, 26 extend in the same direction.Therefore, the further waveguide 26 also extends in the longitudinaldirection 28. FIG. 6 shows a situation where light is adiabaticallycoupled from the waveguide 5 to the further waveguide 26. When the lighttravels along the waveguide 5 it finally arrives at the tapered section27. In the tapered section 27 the light mode 10 can't travel as beforein the waveguide 5. Therefore, the light will couple to the furtherwaveguide 26.

In an alternative, light is coupled from the further waveguide 26 to thewaveguide 5. In this case the further waveguide 26 can comprise atapered section.

In an alternative, both waveguides 5, 26 may contain tapered sections27.

FIG. 7 shows a cross-sectional view of a further device 1 forpropagating light. The insulating layer 3 comprises front-end electroniccomponents 34. As an example a field-effect transistor (FET) 29 isdepicted. The front-end-of-line (FEOL) is the first portion ofintegrated circuit (IC) fabrication where the individual devices(transistors, capacitors, resistors, etc.) are patterned in thesemiconductor. The insulating layer 3 can further comprise an additionalwaveguide 30.

The device 1 can further comprise a passivation layer 31 on top of theinsulating layer 3. The passivation layer 31 is also called isolationlayer. The passivation layer can comprise silicon nitride. Thepassivation layer 31 is used to shield the front-end electroniccomponents 34 from the back-end-of-line wiring and contaminants. Theback-end-of-line (BEOL) is the second portion of integrated circuit (IC)fabrication where the individual devices (transistors, capacitors,resistors, etc.) get interconnected with wiring on the wafer.

The device 1 can further comprise back-end electronic components 32which are arranged above the passivation layer 31. Such back-endelectronic components are for example structured metal layers.Electrical contacts 33 are used to contact the front-end electroniccomponents 34 with the back-end electronic components 32.

Furthermore, the back-end electronic components 32 can comprise a firstinterlayer dielectric (ILD1). Between the structured metal layersdielectric layers can be arranged to shield different structured metallayers from each other.

FIG. 8 shows a cross-sectional view of a further device 1 forpropagating light. The device 1 is coupled to a further waveguide 26. Incontrast to, for example FIG. 7, the propagation direction of the lightis from left to right or from right to left depending if the light iscoupled from the further waveguide 26 to the waveguide 5 or vice versa.

The further waveguide 26 can comprise a waveguide core 35 and a cladding36. The waveguide core 35 can comprise polysilicon, silicon or apolymer. The waveguide core 35 is in direct contact with the waveguide 5in the area where the light couples between the two waveguides 5, 26. Ascan be seen in FIG. 8 the filler material 6 is above the waveguide 5 andabove the waveguide 5 is the substrate 2. The device 1 is supported by acarrier 37. The back-end electronic components 32 are in contact withthe carrier 37 by coupling structures 38, e.g. C4 solder bumps. Thecoupling structures 38 can provide mechanical stability and electriccontacts.

FIG. 9A to 9I show a method for fabricating a device 1 for propagatinglight.

FIG. 9A shows a step S1 of the method. First a semiconductor oninsulator wafer (SOI-wafer) is provided. The SOI-wafer comprises asilicon layer 39, a silicon dioxide layer 40 and a top silicon layer 41on top of the silicon dioxide layer 40. On the top silicon layer 41 afurther silicon dioxide layer 42 is grown. Afterwards a silicon nitridelayer 43 is grown on the silicon dioxide layer 42.

FIG. 9B shows a step S2 of the method. A photoresist 44 is deposited onthe silicon nitride layer 43 and lithographically structured. Trenches45 are etched with the silicon dioxide layer 40 as stop layer.

FIG. 9C shows a step S3 of the method. The photoresist 44 is strippedaway. The trenches 45 are filled using the shallow-trench isolation(STI) electrical isolation scheme. The STI fill 46 consists of silicondioxide deposited using a high-density plasma (HDP).

FIG. 9D shows a step S4 of the method. A chemical-mechanical polishingis performed to provide a planar surface 47.

FIG. 9E shows how a body contact can be realized. That means how acontact to the silicon layer 39 is provided. A photoresist 44 isdeposited on the planar surface 47 and lithographically structured. Thenthe via 48 is etched with the silicon layer 39 as the stop layer.

FIG. 9F shows a step S5 of the method which is carried out analog to therealization of a body contact as depicted in FIG. 9E. However, in thiscase a wider via 49 is etched. The width 50 of the wider via is between1 to 100 μm, more preferably between 5 and 20 μm.

FIG. 9G shows a step S6 of the method. A part of the silicon layer 39 isremoved or transformed to provide the recess 4. Afterwards the recess 4is at least partly filled with the filler material 6. The fillermaterial 6 can be silicon dioxide. Preferably, the filler material 6 isthermally grown in a wet atmosphere. In an alternative, the fillermaterial 6 may be grown through a dry atmosphere at elevatedtemperatures.

FIG. 9H shows a step S7 of the method. The photoresist 44 is strippedaway. Further, the areas 25 between the filler material 6 and thesilicon dioxide layer 40 are filled with silicon dioxide. Afterwards achemical-mechanical polishing is performed to provide a planar surface47.

FIG. 9I shows a step S8 of the method. Next the FEOL processing can beperformed. After the FEOL processing no other processing steps need tobe adjusted or introduced. A passivation layer 31 is then deposited onthe silicon dioxide layer 40 which is the insulating layer 3. Further,the BEOL processing is performed. As shown in FIG. 9I an ILD1 51comprising silicon dioxide is deposited.

Afterwards to finish the fabrication of the device 1 the ILD1 51 has tobe removed in the area over the recess 4 and the waveguide 5 has to bearranged on top of the filler material 6.

More generally, while the present invention has been described withreference to certain embodiments, it will be understood by those skilledin the art that various changes may be made and equivalents may besubstituted without departing from the scope of the present invention.In addition, many modifications may be made to adapt a particularsituation to the teachings of the present invention without departingfrom its scope. Therefore, it is intended that the present invention notbe limited to the particular embodiments disclosed, but that the presentinvention will include all embodiments falling within the scope of theappended claims.

REFERENCE SIGNS

-   1 device-   2 substrate-   3 insulating layer-   4 recess-   5 waveguide-   6 filler material-   7 recess bottom-   8 distance between waveguide and recess bottom-   9 thickness of the insulating layer-   10 light mode-   11 radius of the light mode-   12 width of the recess-   13 area-   14 distance between waveguide and interface-   15 interface between semiconductor material and filler material-   16 semiconductor material-   17 first side wall-   18 second side wall-   19 distance between waveguide and first side wall-   20 distance between waveguide and second side wall-   21 tapered form-   22 straight sidewall-   23 tapered sidewall in the substrate-   24 tapered sidewall in the insulating layer-   25 area-   26 further waveguide-   27 tapered section-   28 longitudinal direction-   29 field-effect transistor-   30 additional waveguide-   31 passivation layer-   32 back-end electronic components-   33 electrical contacts-   34 front-end electronic components-   35 waveguide core-   36 cladding-   37 carrier-   38 coupling structure-   39 silicon layer-   40 silicon dioxide layer-   41 top silicon layer-   42 silicon dioxide layer-   43 silicon nitride layer-   44 photoresist-   45 trench-   46 shallow-trench isolation fill (STI fill)-   47 planar surface-   48 via-   49 wider via-   50 width-   51 interlayer dielectric 1 (ILD1)-   52 cladding-   53 top surface-   54 side surface

The invention claimed is:
 1. A device for propagating light, comprising:a substrate having a semiconductor material; an insulating layer,wherein the insulating layer is arranged on the substrate; a recessformed to penetrate both of a portion of the insulating layer and aportion of the substrate, wherein the recess is at least partiallyfilled with a filler material; and a waveguide arranged on the fillermaterial, wherein a bottom surface of the waveguide is coplanar with atop surface of the insulating layer, wherein the recess has a recessbottom, and a distance between the waveguide and the recess bottom islarger than a thickness of the insulating layer.
 2. A device forpropagating light, comprising: a substrate having a semiconductormaterial; an insulating layer, wherein the insulating layer is arrangedon the substrate; a recess formed to penetrate both of a portion of theinsulating layer and a portion of the substrate, wherein the recess isat least partially filled with a filler material; and a waveguidearranged on the filler material, wherein a bottom surface of thewaveguide is coplanar with a top surface of the insulating layer,wherein the recess is formed such that a distance between the waveguideand an interface between the semiconductor material and the fillermaterial is larger than a radius of a light mode of the waveguide. 3.The device of claim 1, wherein the filler material has a lower index ofrefraction than the substrate.
 4. The device of claim 1, wherein theinsulating layer is a buried oxide layer.
 5. The device of claim 1,wherein the recess has a tapered form in the substrate in a directionfrom the waveguide towards the substrate.
 6. The device of claim 1,wherein a further waveguide is arranged below or above the waveguide foran adiabatic coupling of light between the two waveguides.
 7. The deviceof claim 6, wherein the waveguide extends in a longitudinal directionand the waveguide or the further waveguide is tapered in thelongitudinal direction.
 8. The device of claim 1, wherein the insulatinglayer comprises front-end electronic components.
 9. The device of claim1, further comprising a passivation layer on top of the insulatinglayer.
 10. The device of claim 9, further comprising back-end electroniccomponents above the passivation layer.
 11. The device of claim 10,wherein the back-end electronic components comprise a first interlayerdielectric (ILD1).
 12. The device of claim 1, wherein the fillermaterial and the insulating layer comprise the same material,particularly silicon dioxide, and the substrate comprises silicon. 13.The device of claim 1, wherein the waveguide comprises silicon,polysilicon or a polymer.